<> "The repository administrator has not yet configured an RDF license."^^ . <> . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE"^^ . "ABSTRACT\r\nThe research was conducted about fabrication and characterization NiO/Ag thin films as a\r\nphotocatalyst degradation of methylene blue dye. This study aims to producted NiO/Ag thin films\r\nwhich prepared by RF sputtering technique at a frequency 13.56 MHz on characterize their\r\ncrystallinity, morphological, composition and optical properties then used as a photocatalyst\r\ndegradation of methylene blue dye. NiO/Ag thin films were growth on glass substrates by RF\r\nsputtering technique on frequency 13.56 MHz. NiO/Ag thin films were grown on glass substrates\r\nwith variation of oxygen pressure at (0.05; 0.1; 0.15) × 10-2 mbar with time deposition 1 minute for\r\nUV-Vis analysis and oxygen pressure at 0.1 × 10-2 mbar with time deposition 15 minutes for XRD,\r\nSEM and EDX analysis. XRD analysis showed that stronger intensity thin film NiO/Ag of (111) and\r\n(200) planes at peak positioned 2θ of 37,660 and 43,230. SEM analysis, the particle NiO/Ag thin\r\nfilms was homogeneous in the surface region with a diameter crystal 50.8 nm. EDX analysis of\r\nNiO/Ag thin films showed that the Ni = 40.45%, Ag = 13.01% and O = 46.53%. Based on UV-Vis\r\nanalysis variation of oxygen pressure, band gap energy was 2,8 eV, 3,1 eV and 3,2 eV. Degradation\r\ntest of methylene blue using NiO/Ag thin films and the degradation time during 4 hours. Methylene\r\nblue degradation showed that 88,229 %, 89,86% dan 91,956% for variation oxygen pressure at\r\n(0.05; 0.1; 0.15) × 10-2 mbar. It was concluded that was NiO/Ag thin films able to degradated dye\r\nmethylene blue. Based on the research oxygen pressure on 0,15 × 10-2 mbar is the highest, intensty\r\ndegradation at 91,956%.\r\nKeywords: NiO/Ag thin films, photocatalytic degradation, methylene blue\r\nINTISARI\r\nTelah dilakukan penelitian tentang fabrikasi dan karakterisasi lapisan tipis NiO/Ag sebagai\r\nfotokatalis degradasi zat warna methylene blue. Penelitian ini dikerjakan dengan membuat lapisan\r\ntipis NiO/Ag yang dideposisikan menggunakan metode RF-Sputtering pada frekuensi 13,56 MHz.\r\nKemudian mengkarakterisasinya untuk mengetahui kristalinitas, struktur morfologi, komposisi dan\r\nsifat optik serta untuk mendegradasikan methylene blue. Lapisan tipis NiO/Ag berhasil\r\ndideposisikan di atas substrat kaca dengan menggunakan RF sputtering. Penumbuhan lapisan tipis\r\ndi atas substrat kaca dengan menvariasikan tekanan oksigen (0,05; 0,1; 0,15) × 10-2 mbar selama 1\r\nmenit untuk analisis UV-Vis dan tekanan oksigen 0,1 × 10-2 mbar dengan waktu deposisi 15 menit\r\nuntuk analisis XRD, SEM dan EDX. Analisis XRD menunjukan bahwa intensitas tertinggi pada\r\nbidang (111) dan (200) yang berada pada puncak 2θ 37,660 dan 43,230. Lapisan tipis NiO/Ag\r\nmemiliki morfologi yang homogen dengan diameter kristal NiO/Ag 50,8 nm. Analisis EDX\r\nmenunjukan persentase massa elemen Ni = 40,45%, Ag = 13,01% dan O = 46,53%. Analisis UVVis\r\ndengan variasi tekanan oksigen didapat energi celah pita dari lapisan tipis NiO/Ag, yaitu 2,8 eV,\r\n3,1 eV dan 3,2 eV. Uji fotodegradasi methylene blue menggunakan lapisan tipis NiO/Ag dengan\r\nwaktu degradasi selama 4 jam penyinaran UV. Degradasi methylene blue menunjukan hasil dengan\r\npersentase 88,229 %, 89,86% dan 91,956% untuk masing-masing tekanan oksigen (0,05; 0,1; 0,15)\r\n× 10-2 mbar. Penelitian ini menyimpulkan bahwa lapisan tipis NiO/Ag dapat mendegradasi zat warna\r\nmethylene blue dan lapisan tipis dengan tekanan oksigen 0,15× 10-2 mbar memiliki persentase\r\ndegradasi paling tinggi sebesar 91,956%.\r\nKata Kunci: Lapisan Tipis NiO/Ag, Degradasi fotokatalis, methylene blue"^^ . "2019-08-05" . . . . "UIN Sunan Kalijaga"^^ . . . "Fakultas Sains dan Teknologi, UIN Sunan Kalijaga"^^ . . . . . . . . . "NIM 15620010"^^ . "Lizara Carina Sardy"^^ . "NIM 15620010 Lizara Carina Sardy"^^ . . . . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Text)"^^ . . . . . "15620010_BAB I_IV-atau_DAFTAR-PUSTAKA.pdf"^^ . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Text)"^^ . . . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "preview.jpg"^^ . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "medium.jpg"^^ . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . . "small.jpg"^^ . . . "FABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag\r\nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA\r\nMETHYLENE BLUE (Other)"^^ . . . . . "HTML Summary of #37572 \n\nFABRIKASI DAN KARAKTERISASI LAPISAN TIPIS NiO/Ag \nSEBAGAI FOTOKATALIS DEGRADASI ZAT WARNA \nMETHYLENE BLUE\n\n" . "text/html" . . . "Fisika"@en . .