%T SEBAGAI FOTOKATALIS NANOPARTIKEL UNTUK MENURUNKAN KADAR COD, BOD DAN TSS LIMBAH CAIR INDUSTRI ETANOL (Vinasse)
%U https://digilib.uin-suka.ac.id/id/eprint/56287/
%X nanoparticle photocatalyst to reduce COD, BOD and TSS levels of ethanol  industrial liquid waste (vinasse) has been done.This study aims to determine the  character of the TiO2-zeolite composite using X-Ray Diffraction (XRD), Infrared  Fourier Transform (FTIR), and UV-Visible Diffuse Reflectance (UV-Vis DRS), to  determine the activity of TiO2-zeolite photocatalyst against photodegradation of  ethanol industrial wastewater with variations in photodegradation reaction  conditions, weight of TiO2-zeolite composite and temperature of ethanol industrial  liquid waste, to determine the photocatalyst ability of TiO2-zeolite in degrading  ethanol industrial wastewater with levels of COD, BOD, TSS and pH against  quality standards. Natural zeolite is activated using sulfuric acid (H2SO4) as TiO2  carrier and composites were made by synthesis using inclusion oligocation method.  The test material includes characterization with XRD, FTIR and UV-Vis  DRS. Characterization of TiO2-zeolite seen in the results of the characteristics using  XRD indicates the presence of a spectral peak belonging to rutile in the TiO2-zeolite  composite, with a composite size of 29,47 nm. Characterization by FTIR the  appearance of absorption at a wave number of 570,93 cm-1 and 2368,59 cm-1 which  is the absorption of TiO2. Characterization with UV-Vis DRS showed a decrease in  band gap after TiO2 development to 2,9 eV.  Photodegradation of ethanol industrial liquid waste was carried out with  variations of photodegradation reaction conditions, weight of TiO2-zeolite  composite and temperature of ethanol industrial wastewater and temperature at 30,  60, 90 and 120 minutes. The order kinetics of the photodegradation reaction of  ethanol industrial liquid waste (vinasse) that occurs follow the second order. After  photodegradation, the pH value remained at 4.3, and the levels of COD, BOD and  TSS decreased with low photocatalytic activity. The decline that occurs still does  not meet the quality standards based on the Regulation of the Minister of  Environment of the Republic of Indonesia No. 5 of 2014.
%Z Pembimbing: Didik Krisdiyanto, S.Si., M.Sc.